Эпоксидный Покрытия Пола \ Em-Poxy PK 7200 Для текстурированных приложений

Ürün Teknik Dökümanları
Descriptiopn
It is a double-component, epoxy resin-based, textured (orange peel effect) floor coating containing a very small amount of solvent.
 
Usage Areas
• As a top coat; on concrete surfaces,
• In base coated systems rugged with sand,
• In areas requiring a nonskid and easy-to-clean surface,
• In production and storage areas, garages, hangars and loading ramps,
• In parking areas,
• At hospitals,
• In kitchens,
• In data processing and control centers.
Surface Preparation
• Pressure strength of the concrete to be treated must be 25 N/mm2 minimum and tensile strength 1,5 N/mm2 minimum.
• The humidity ratio in the concrete must be lower than 5%.
• Potential movements must be considered in designing joints and whereever necessary joints must be transferred to coating.
• The surface to be treated must be clean and dry and free from any other substance such as dirt, grease, old coatings and curing materials.
• Gaps and holes must be completely cleared first and then filled with Em-Poxy A or Em-Poxy WB which is prepared in paste form by adding sand.
• To ensure a smooth surface any swelling must be levelled.
• All dust and loose and displaced particles must be removed by using a brush and/or vacuum cleaner.
• Concrete surfaces must be undercoated with Em-Poxy A. (Make sure the surface is primed with a seamless and poreless undercoat. Apply the undercoat with a brush or roller.)
• During application relative humidity must not exceed 50% when the ambient temperature is +10°C, and 80% when the ambient temperature is +30°C.
• The temperature of the surface to be treated must be between +10°C and +30°C.
• The temperature of the surface to be treated must be 3°C higher than the dew point.
• Ambient temperature and surface temperature must be increased by using heaters for the applications performed in cold weather conditions and Em-Poxy PK containers must be kept under +20°C the previous night.
Application
First stir Component A and Component B separately, and then add Component B to Component A and stir the mixture continuously to a homogenous consistency with a low speed mixer for 3 minutes. To minimize air drag avoid stirring too much.
The mixture should be applied to the prepared surface with a coral roller in two coats and the thickness of each coat must be 200 microns. It is critical to apply the second coat on time. Otherwise decreased adherence may lead to cleavage. If the edges match ‘wet’ during application, a seamless effect can be created.
Consumption
Approximately 0,600 kg/m2 in two coats depending on the absorbance of the surface to be treated.
Packaging
Component A + Component B = Net 12,5 kg as a set

 